Anti-corrosion semi-matte paint, anthracite, 2,5L

Anthracite anti-corrosion semi-matt paint suitable for zinc and aluminum.
The paint is compatible with the spray J08/01-ANTHRACITE

WS-Plast® Thick Film M 4200 is a pure acrylate paint system which, due to its special composition, adheres to zinc and aluminum surfaces without any primer.
It is suitable for use as a duplex system (hot dip galvanizing plus coating) depending on the layer thickness and the ambient conditions for coating acc. to EN ISO 12944.
It is also suitable for coatings of hot-dip galvanized enclosures, gates, balcony railings, lamps, gutters, steel structures, blacksmithing, as well as non-anodized aluminum components such as porches, flagpoles, cladding, etc.
Always electrostatically adjusted. WS-Plast® thick film M 4200 can be rolled, sprayed or painted.

Surface preparation:
For hot-dip galvanized surfaces, aluminum surfaces, non-galvanized steel and old coatings, different pretreatments should be used. Please note the product data sheet and the processing information.

Application:
The processing can be done by brushing, rolling, conventional or airless spraying. All electrostatic methods are applicable. Stir well before use. For further information (dilution, injection pressure, etc.) please refer to the product data sheet and the processing information.
Drying time:
Dust-dry: approx. 20 minutes
Recoatable: approx. 1-2 hours
Touch proof: about 2 hours
Completely dry: about 1-2 days

Productiveness:
250 g per m2 result in 80my dry film = the recommended minimum layer thickness. When used near the coast and in road salt contaminated environment at least 160my are required.